Comparative Study of Electrospun Scaffolds Containing Native GAGs and a GAG Mimetic for Human Mesenchymal Stem Cell Chondrogenesis

Document Type

Article

Publication Date

7-1-2020

Abstract

Articular cartilage has limited healing and self-repair capability. Damage to articular cartilage becomes irreversible leading to osteoarthritis, which can impact a person’s quality of life. Approximately, 5–10% of cartilage tissue is made up of sulfated glycosaminoglycans (GAGs), which sequester growth factors as well as provide structural integrity to the native cartilage tissue. This study evaluated the chondrogenic differentiation of human mesenchymal stem cells (MSCs) on gelatin-based scaffolds containing partially sulfated cellulose (pSC), a GAG mimetic derived from cellulose, in comparison to native GAGs, chondroitin sulfate-A (CS-A) and chondroitin sulfate-C (CS-C), where pSC has similarity to CS-C in terms of degree and pattern of sulfation. Scaffolds were prepared by electrospinning gelatin with pSC or the native GAGs. All scaffolds consist of fibers having average diameters of approximately 3 μm and inter-fiber spacing of approximately 30 μm and were hydrolytically stable throughout the culture. MSCs cultured on pSC containing scaffolds showed early production of sulfated GAGs and higher collagen type II to type I ratio than native GAGs. Among the native GAGs, chondrogenesis was promoted to a greater extent for CS-C in comparison to CS-A containing scaffolds, which suggests the pattern of sulfation impacts chondrogenesis. Partially sulfated cellulose could be used as a potential GAG mimic for cartilage tissue engineering applications.

Identifier

85083331344 (Scopus)

Publication Title

Annals of Biomedical Engineering

External Full Text Location

https://doi.org/10.1007/s10439-020-02499-9

e-ISSN

15739686

ISSN

00906964

PubMed ID

32285342

First Page

2040

Last Page

2052

Issue

7

Volume

48

Grant

1207173

Fund Ref

National Science Foundation

This document is currently not available here.

Share

COinS